Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom

All Products

Kiln Refractory Material (10)

Castable Refractory Cement (15)

Insulating Castable (12)

Diatomite Bricks (14)

Corundum Mullite (14)

Light Weight Clay Bricks (14)

High Alumina Bricks (10)

Mullite Bricks (12)

High Alumina Refractory (10)

Fire Clay Bricks (10)

Insulation Ceramic Fiber (12)

Fiber Glass Wool (15)

Inert Alumina Balls (12)

I'm Online Chat Now

Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom

Name: Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom
Brand: WeiHang
SKU: WeiHang
Price: 1.00 USD
Availability: InStock
Rating: 4.6 (192 reviews)

$Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom$

$Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom$

Large Image : Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom

Product Details:

Brand Name:	WeiHang

Payment & Shipping Terms:

Minimum Order Quantity:	1000 Piece/Pieces
Price:	negotiation
Payment Terms:	L/C, T/T

Contact Now

Detailed Product Description

Apparent Porosity::	20-22%	Cold Crushing Streng:	60Mpa
Bulk Density::	2.4-2.6g/cm3	Material::	Alumina Block
Model Number::	Customer's Requirement	Refractoriness (Degree)::	1580°< Refractoriness< 1770°
High Light:	lightweight fire brick , mullite insulating brick

High Alumina Refractory Fire Brick Insulating Brick

Standard sizing: 230 x 114 x 65 mm ,Special size and OEM Service also provide!

The size is precise, providing kinds of shapes according to customer's drawing

High Alumina Bricks manufacturing process is similar to much grog clay brick, the different is there are higher proportion of grog in ingredients that can reach 90~95%. Select and screening deironing before the grog crushed. Firing temperature is higher, as of Grade I &II high alumina bricks fired in the tunnel kiln is 1500~1600 ℃.Chinese production practice shows that select, grading and keep in storage high alumina grog before crushed. Adopt fine grinding methods calcined bauxite and mixed clay to improve product's quality.

Item		Unit	Wear-resistant refractory brick
Item		Unit	NMZ-1	NMZ-2	NMZ-3
Chemical composition	Al2O₃	%	≥85	≥75	≥65
	SiO₂	%	≤15	≤25	≤35
	Fe₂O₃	%	＜1.0	≤1.2	≤1.5
Density		g/cm³	≥2.9	≥2.6	≥2.5
Compressive strength (normal temperature)		Mpa	≥100	≥85	≥70
Apparent porosity		％	≤18	≤20	≤21
Abrasion resistance		cc	≤6	≤7	≤8
Refractoriness		℃	≥1790	≥1790	≥1790
Linear change on heating (900℃×3h)		％	≤0.05	≤0.1	≤0.1
Thermal conductivity(350℃)		w/m.k	≤1.8	≤1.8	≤1.5
Thermal shock stability(1100℃Water cooling)		次	20	20	20

$Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom 0$

Details:

1. Made by flint clay clinker and binder,through Crushing,Mixing,Shaping,Drying and high temperature Sintering.

2. Al2O3 content is 30%-48%,SiO2 content is 50%-65%,and a small number of alkali metals,alkaline earthmetal oxides TiO2,Fe2O3 etc.3.Working temperature:less than 1350°C.

Features:

1. Good resistance to abrasion and corrosion,

2. Good volume stability at high temperature,

3. Chemical attack to provide long service life,

4. Easy operation and installation,

5. Broad usage or applications and low price.

Application

It is widely used for steel industry, cement and ceramics industry, glass plant, power industry, metallrgy petrochemical inustry, etc.

Certificate

$Ceramics Industry Diatomite Bricks High Alumina Refractory Bricks Custom 1$

Tag:

Contact Person: Pan Junhui

Tel: +86 15861509962

Fax: 86-0510-87441369

Other Products

Lightweight Insulating Fire Clay Brick ECO Friendly Gasification Furnace

Apparent Porosity:: 20-22%

Cold Crushing Streng: 60Mpa

Bulk Density:: 2.4-2.6g/cm3