Kiln Refractory Material & Castable Refractory Cement

$Cement Industry Kiln Refractory Material Bauxite Corundum Mullite Brick$

Cement Industry Kiln Refractory Material Bauxite Corundum Mullite Brick
- Refractoriness (Degree):: Common (1580°< Refractoriness< 1770°)
- Density (g/cm3):: 2.05-2.75
- Permanent Linear Change % 1500CX2h: -0.5%~+0.1%
- 0.2 MPa Refractoriness Under Load: ≥1350℃
$Basic Kiln Refractory Material Alumina Light Weight Brick 35%-40% Al2O3 Content$

Basic Kiln Refractory Material Alumina Light Weight Brick 35%-40% Al2O3 Content
- Refractoriness (Degree):: Common (1580°< Refractoriness< 1770°)
- Density (g/cm3):: 2.05-2.75
- Permanent Linear Change % 1500CX2h: -0.5%~+0.1%
- 0.2 MPa Refractoriness Under Load: ≥1350℃
$Wearing Resistant Alumina Castable Refractory Cement Light Weight$

Wearing Resistant Alumina Castable Refractory Cement Light Weight
- Material:: Alumina Block
- Product Name:: Corundum Castable
- Application:: Industrial Furnace
- Granulometric Class:: ≤5mm
$Insulating Castable Refractory Mortar Good Slag Resistance Good Hot Strength$

Insulating Castable Refractory Mortar Good Slag Resistance Good Hot Strength
- Material:: Alumina Block
- Product Name:: Corundum Castable
- Application:: Industrial Furnace
- Granulometric Class:: ≤5mm
$High Strength Refractory Insulating Castable Furnace Steel Groove Liner$

High Strength Refractory Insulating Castable Furnace Steel Groove Liner
- Usage: Hot Blast Stove
- Max Service Temperature: 1600
- Quality: Super Class
- MgO Content (%): 0.8-1.2%
$Energy Saving Green Castable Refractory Cement Recipe Light Weight Refractory Concrete$

Energy Saving Green Castable Refractory Cement Recipe Light Weight Refractory Concrete
Low Thermal Conductivity Diatomite Bricks Heat Retaining Clay Insulating Fire Brick
- Apparent Porosity:: 20-22%
- Cold Crushing Streng: 60Mpa
- Bulk Density:: 2.4-2.6g/cm3
- Product Name:: Insulating Brick
Custom Made Mullite Insulation Brick High Temp For Blast And Glass Furnace
- Al2O3 Content (%):: 35%-73.4%
- Size:: Custom-Made
- Name: Mullite Insulating Bricks
- Bulk Density, G/cm3: 0.45-1.02
$Refractory Material Mud Light Weight Clay Bricks For Furnace Construction$

Refractory Material Mud Light Weight Clay Bricks For Furnace Construction
- Refractoriness (Degree):: Common (1580°< Refractoriness< 1770°)
- Density (g/cm3):: 2.05-2.75
- Permanent Linear Change % 1500CX2h: -0.5%~+0.1%
- 0.2 MPa Refractoriness Under Load: ≥1350℃
$Heat Retaining Light Weight Fire Brick High Aluminum Refractory Furnace Lining Insulating$

Heat Retaining Light Weight Fire Brick High Aluminum Refractory Furnace Lining Insulating
- Apparent Porosity:: 20-22%
- Cold Crushing Streng: 60Mpa
- Bulk Density:: 2.4-2.6g/cm3
- Material:: Alumina Block
$Mullite Insulating Basic Refractory Bricks Yellow Fire Brick Lower Bulk Density$

Mullite Insulating Basic Refractory Bricks Yellow Fire Brick Lower Bulk Density
- Refractoriness (Degree): 1770°< Refractoriness< 2000°
- Cold Cushing Strength (mpa): ≥90
- Rervice Temperature: 1500
- 0.2MP Refractoriness Under Load: 1500
$High Temp Spinel Bricks High Alumina Refractory For Lime Kiln Furnace Boiler Oven$

High Temp Spinel Bricks High Alumina Refractory For Lime Kiln Furnace Boiler Oven
- Refractoriness (Degree): 1770°< Refractoriness< 2000°
- Linear Change(%),oC*2h: 1300~1580
- Product Name: Insulating Refractory Brick
- Size: Customizable

Who We Are

Introduction

Jiangsu weihang energy-saving technology co., LTD. (wuxi huatai refractory engineering co., LTD.) is located in the beautiful and fertile pottery city of yixing city in the eastern suburbs, is located ...

QC QC Profile

The quality of our products is checked by the inspection of the exported products and 100% of the total inspections are conducted. Choosing us means choosing high quality products and excellent ...

Contact Us

Address : Beitang, Dingshu Town, Yixing City, Jiangsu Province

Worktime: 8:00-17:00 ( Beijing time)

FAX : 86-0510-87441369

Email : 15861509962@163.com

Jiangsu Weihang Energy Sabing Technology Co.,Ltd.